The Image Analyses Utilization at Nickel-base Superalloy Degradation Classification
Řičánková, Veronika ; Juliš, Martin (referee) ; Němec, Karel (advisor)
During operational conditions of internal combustion turbines of turbojet engines, the impeller blades are stressed by load cycles which vary in time, temperature and stress. In the course of operation, the blades are exposed to a considerable number of degradation effects, particularly high-temperature corrosion, fatigue processes and creep. The presented work is aimed at the study of the structure cast nickel-base superalloy INCONEL 713 LC, creep tests exposured. The structural changes (degradation) was clasifikation by the help of image analyses. Operational conditions of heat parts, used in gas turbines and turbo-compressors, were simulated by creep tests of Inconel 713 LC nickel superalloy during a constant load of temperatures ranging from 750 up to 950C. Changes in the structure dependent upon time, temperature and stress applied were analysed by means of light and electron microscopy methods and image analyses after the fracture of test bars.
|
|
|
Classification of microstructure of nickel-base superalloys with image analysis using
Volf, Milan ; Čelko, Ladislav (referee) ; Němec, Karel (advisor)
During operational conditions of internal combustion turbines of turbojet engines, the impeller are stressed by load cycles which vary in time, temperature and stress. In the course of operation, the blades are exposed to a considerable number of degradation effects, particularly high-temperature corrosion, fatigue processes and creep. The presented work is aimed at the study of the structure cast nickel-base superalloy INCONEL 713 LC, creep tests exposured. The structural changes (degradation) was clasification by the help of image analyses. Operational conditions of heat parts, used in gas turbines and turbo-compressors, were simulated by creep tests of Inconel 713 LC nickel superalloy during a constant load of temperatures ranging from 750 up to 950°C. Changes in the structure dependent upon time, temperature and stress applied were analysed by means of light and electron microscopy methods and image analyses after the fracture of test bars.
|
|
|
Low cycle fatigue of nickel superalloy IN713LC with TBC layer at high temperatures
Machala, Jan ; Čelko, Ladislav (referee) ; Juliš, Martin (advisor)
This thesis deals with the low cycle fatigue nickel-based superalloy IN713LC with applied TBC barrier at high temperature. The theoretical part is divided into four sections. The first one focuses on description of fatigue damage. The second one provides the basic characteristics of nickel-based superalloys. The third section describes the use of the surface layers - diffusion layers and thermal barriers and the fourth section deals with the influence of these layers on fatigue properties. Experimental part is focused on the evaluation of low cycle fatigue tests and on the explanation of the mechanisms of initiation and propagation of fatigue cracks. For the experimental part, fatigue samples were prepared by vacuum precision investment casting. TBC barrier was applied by atmospheric plasma spraying and consists of two sublayers - the lower metallic bond coating type CoNiCrAlY and top ceramic coating type YSZ. Low cycle fatigue tests were conducted under strain control at controlled temperature of 900 ° C. Fractographical analysis of fracture surfaces was carried out by using light and electron microscopy. Effect of applied barrier to fatigue life was determined - the parameters of Manson-Coffin and Basquin curve. A cyclic stress-strain curve was also obtained. The curves softening / hardening and number of transit cycles were determined. The obtained parameters and values from fatigue tests were compared with available data from fatigue tests of superalloy IN713LC without the layer, as applied AlSi type diffusion layer, at high temperatures. The initiation site on the fracture surfaces was determined within the fractographic evaluation and the influence of the layer on the initiation and propagation of fatigue cracks was discussed. A helpful tool was the assessment of longitudinal sections using scanning electron microscopy.
|
|
|
Low cycle fatigue of nickel superalloy IN713LC with TBC layer at high temperatures
Machala, Jan ; Čelko, Ladislav (referee) ; Juliš, Martin (advisor)
This thesis deals with the low cycle fatigue nickel-based superalloy IN713LC with applied TBC barrier at high temperature. The theoretical part is divided into four sections. The first one focuses on description of fatigue damage. The second one provides the basic characteristics of nickel-based superalloys. The third section describes the use of the surface layers - diffusion layers and thermal barriers and the fourth section deals with the influence of these layers on fatigue properties. Experimental part is focused on the evaluation of low cycle fatigue tests and on the explanation of the mechanisms of initiation and propagation of fatigue cracks. For the experimental part, fatigue samples were prepared by vacuum precision investment casting. TBC barrier was applied by atmospheric plasma spraying and consists of two sublayers - the lower metallic bond coating type CoNiCrAlY and top ceramic coating type YSZ. Low cycle fatigue tests were conducted under strain control at controlled temperature of 900 ° C. Fractographical analysis of fracture surfaces was carried out by using light and electron microscopy. Effect of applied barrier to fatigue life was determined - the parameters of Manson-Coffin and Basquin curve. A cyclic stress-strain curve was also obtained. The curves softening / hardening and number of transit cycles were determined. The obtained parameters and values from fatigue tests were compared with available data from fatigue tests of superalloy IN713LC without the layer, as applied AlSi type diffusion layer, at high temperatures. The initiation site on the fracture surfaces was determined within the fractographic evaluation and the influence of the layer on the initiation and propagation of fatigue cracks was discussed. A helpful tool was the assessment of longitudinal sections using scanning electron microscopy.
|
|
|
Classification of microstructure of nickel-base superalloys with image analysis using
Volf, Milan ; Čelko, Ladislav (referee) ; Němec, Karel (advisor)
During operational conditions of internal combustion turbines of turbojet engines, the impeller are stressed by load cycles which vary in time, temperature and stress. In the course of operation, the blades are exposed to a considerable number of degradation effects, particularly high-temperature corrosion, fatigue processes and creep. The presented work is aimed at the study of the structure cast nickel-base superalloy INCONEL 713 LC, creep tests exposured. The structural changes (degradation) was clasification by the help of image analyses. Operational conditions of heat parts, used in gas turbines and turbo-compressors, were simulated by creep tests of Inconel 713 LC nickel superalloy during a constant load of temperatures ranging from 750 up to 950°C. Changes in the structure dependent upon time, temperature and stress applied were analysed by means of light and electron microscopy methods and image analyses after the fracture of test bars.
|
|
|
The Image Analyses Utilization at Nickel-base Superalloy Degradation Classification
Řičánková, Veronika ; Juliš, Martin (referee) ; Němec, Karel (advisor)
During operational conditions of internal combustion turbines of turbojet engines, the impeller blades are stressed by load cycles which vary in time, temperature and stress. In the course of operation, the blades are exposed to a considerable number of degradation effects, particularly high-temperature corrosion, fatigue processes and creep. The presented work is aimed at the study of the structure cast nickel-base superalloy INCONEL 713 LC, creep tests exposured. The structural changes (degradation) was clasifikation by the help of image analyses. Operational conditions of heat parts, used in gas turbines and turbo-compressors, were simulated by creep tests of Inconel 713 LC nickel superalloy during a constant load of temperatures ranging from 750 up to 950C. Changes in the structure dependent upon time, temperature and stress applied were analysed by means of light and electron microscopy methods and image analyses after the fracture of test bars.
|